Hot Dip Galvanized Coil

Hot Dip Galvanized Coil Description

Hot dip galvanizing is to make the molten metal react with the iron substrate to produce an alloy layer, so that the substrate and the coating are combined. Hot galvanizing is to pickle the steel and iron parts first. In order to remove the iron oxide on the surface of the steel and iron parts, after pickling, it is cleaned by ammonium chloride or zinc chloride aqueous solution or ammonium chloride and zinc chloride mixed aqueous solution tank, and then sent into the hot dip plating tank. Hot-dip galvanizing has the advantages of uniform coating, strong adhesion and long service life.
Hot-dip galvanizing is one of the effective means to delay the environmental corrosion of iron and steel materials, it is the surface of the cleaned, activated iron and steel products immersed in molten zinc, through the reaction and diffusion between iron and zinc, in the iron and steel products surface plating good adhesion of zinc alloy coating. Compared with other metal protection methods, the hot-dip galvanizing process has advantages in the protection characteristics of the combination of physical barrier and electrochemical protection of the coating, the bonding strength of the coating and the substrate, the compactness, durability, maintenance-free and economy of the coating, and its adaptability to the shape and size of the product. At present, hot-dip galvanized products mainly include steel plates, steel strips, steel wires, steel pipes, etc., of which hot-dip galvanized steel plates account for a large proportion.

The production process of hot galvanizing is as follows:
Mother material → degreasing → water washing → pickling → water washing → rinsing → flux solution → drying → hot galvanizing → cooling → inspection → packaging

Standard

Grade

C

Si

Mn

P

S

Ti

Forcold forming

Chinese Standard

DX51D Z

0.12

0.50

0.60

0.100

0.045

0.30

DX52D With

0.12

0.50

0.60

0.100

0.045

0.30

DX53D Z

0.12

0.50

0.60

0.100

0.045

0.30

DX54D Z

0.12

0.50

0.60

0.100

0.045

0.30

DX56D Z

0.12

0.50

0.60

0.100

0.045

0.30

DX57D Z

0.12

0.50

0.60

0.100

0.045

0.30

Forcold forming

Japanese Standard

SGCC

0.15

0.50

0.80

0.050

0.030

0.025

SGCD1
SGCD2

0.12
0.10

0.50
0.50

0.60
0.45

0.040
0.030

0.030
0.030

0.025
0.025

SGCD3

0.08

0.50

0.45

0.030

0.030

0.025

SGCD4

0.06

0.50

0.45

0.030

0.030

0.025

ForStructure

Japanese Standard

SGC340

0.25

0.50

1.70

0.200

0.035

0.025

SGC400
SGC440

0.25
0.25

0.50
0.50

1.70
2.00

0.200
0.200

0.035
0.035

0.150
0.150

SGC490

0.30

0.50

2.00

0.200

0.035

0.025

SGC510

0.30

0.50

2.50

0.200

0.035

0.025

ForStructure

AISI Standard

S220GD Z

0.20

0.60

0.70

0.100

0.045

0.025

S250GD With

0.20

0.60

0.70

0.100

0.045

0.025

S280GD Z

0.20

0.60

0.70

0.100

0.045

0.025

S320GD Z

0.20

0.60

0.70

0.100

0.045

0.025

S350GD Z

0.20

0.60

0.70

0.100

0.045

0.150

S550GD Z

0.20

0.60

0.70

0.100

0.045

0.150

Grade

Yield strength MPa≥

Tensile Strength MPa≥

Elongation A%≥

DX51D Z/ZM/AZ/AM

240-380

270-500

22

DX52D Z/ZM/AZ/AM

140-300

270-420

26

DX53D Z/ZM/AZ/AM

140-260

270-380

30

DX54D Z/ZM/AZ/AM

120-220

260-350

36

S220GD Z/ZM/AM

220

300

20

S250GD Z/ZM/AZ/AM

250

330

19

S280GD Z/ZM/AM

280

360

18

S300GD A/AM

300

380

18

S320GD Z/ZM/AM

320

390

17

S350GD Z/ZM/AZ/AM

350

420

16

S450GD A/AM

450

480

15

S550GD Z/ZM/AZ/AM

550

550

-

Zero Spangle

Minimized Spangle

Normal Spangle

Large Spangle